Heavy Duty Black Geomembrane Tarpaulin for Waterproof Tarps Production

• Customization: Available
• Feature: Anti-UV, Water Proof
• Style: Geomembrane
• Model NO.: Geomembrane
• Thickness: Light Weight
• Use: Transportation Project, Hydraulic Project, Geotech
• Yarn: 1000d*1000d
• Color: Red, Blue, White, Green and Customized
• Length: 50-150m/Roll or as Your Requirement
• Surface: Smooth
• Transport Package: Hard Tube or PE Bag
• Specification: Lacquered, Anti-UV, Anti-Mildew, Anti-Static
• Trademark: jinze
• Origin: China
• HS Code: 6306199090
• Production Capacity: 100000sqm/Month

Product Description

HDPE Geomembrane

HDPE Geomembrane is the low permeable synthetic geomembrane liner and geotechnical engineering materials which are widely used for acquanculture and water containment applications. 

HDPE Geomembrane is made of finest quality high density polyethylene (HDPE) with specially formulated, virgin polyethylene resin, combined with specified quantity carbon black, antioxidant, anti-aging agent and UV resistance components, which makes our smooth geomembrane HDPE Geomembrane with excellent resistance to UV radiation and is suitable for exposed conditions. HDPE Geomembrane is the ideal low permeable synthetic material for Shrimp farming.

Item	Test Value
	RH0.30 mm	RH0.5 mm	RH0.75 mm	RH1.0 mm	RH1.5 mm	RH2.0 mm	RH3.0 mm
Minimum Density(g/cm³)	0.94
Strength at yield,N/mm	5	8	11	15	22	29	44
Strength at break ,N/mm	8	14	20	28	40	53	80
Elongation at yield,%	13
Elongation at break,%	720min
Tear Resistance N	40	65	93	125	190	250	375
Puncture Resistance N	105	176	240	320	480	640	960
Stress Crack Resistance, hrs	300
Carbon Black Content, %	2.0-3.0
Carbon Black Dispersion	1 or 2
Standard OIT Min	100
High Pressure OIT Min	400
85ºC Heat aging(OIT Retention rate at Normal pressure after 90d ) %	85
UV resistance (OIT retention rate after 1600 hours of UV radiation)	65
Impact Cold Crack at -70°C	Pass
Water vapor permeability (g.cm/cm2 .s.Pa)	≤1.0×10-13
Dimensional Stability (%)	±2